Warman pump material A05 is a common material used by Warman pump, A05 is the code for the material, this material also known as High Chrome 27% or KmTBCr27, and US ASTM-A532
Material Type: Erosion resistant white iron
High Chrome 27% is a wear resistant white iron that offers excellent performance under erosive conditions. The alloy can be effectively used in a wide range of slurry types, like mine slurry, power plant, industry waste and etc
As warman pump material, the high wear resistance of High Chrome 27% is provided by the presence of hard carbides within its microstructure. High Chrome 27% is particularly suited to applications where mild corrosion resistance, as well as erosion resistance is required.
Density (kg/m3) 7500
Hardness (HBW 10/3000) 650
Tensile strength (MPa) 780
Young¡ﬂs modulus (GPa) 220
Elongation at break (%) 0.4
Toughness (J) 190
High Chrome 27% is generally not suitable for highly corrosive duties. The alloy can be used in mild corrosive duties, within a pH range of 5 to 12, for silphuric and nitric acids, or sodium hydroxide applications.
High Chrome 27% Parts Availability
Most wet-end slurry pump wear parts can be produced in High Chrome 27%. The most common parts are as follows: Slurry Pump Impellers, Throatbush, Volute liners, Frame plate liner insert, Casings
High-Chrome 27% can be used for pumping a wide range of mild corrosive slurries. The alloy gives very excellent wear life for a wide variety of particle sizes and hardness. Usually, High-Chrome 27% is most cost effective for particles greater than 100um in size.
Contact us to know more of slurry pump, gravel pump and dredge pump, and find out what slurry pump parts, gravel pump parts and dredge pump parts in need.